合金法实现ZnO的P型转化

全部作者： 张景文 王洪波 侯洵 第1作者单位： 西安交通大学 论文摘要： ZnO films were grown on Sapphire and n-type Silicon, and then deposited a gold film in some areas. After heat treatments in the air through gold alloy technics, they were employed to some electrical measurements. After treatment at the temperature of 850°C, ZnO, grown on sapphire and under gold layer, displayed super high resistivity. It seemed that the ZnO, grown on n-Si and under gold layer, displayed p-type conductivity, for diode-like I-V rectifying characteristics were observed between it and n-Si, and the ZnO layer, which was not deposited gold film. During the course of I-V characteristics measurement, the sample, grown on the n-Si and post treated at 750°C, appeared overflow twice, and then was observed stable rectifying characteristic. But the sample post treated at 650°C and lower temperature, was not observed rectifying characteristic. Farther experiment researches require to carried out. 关键词： ZnO films, p-type Conversion, Gold Alloy (浏览全文) 发表日期： 2006年11月29日 同行评议：

（暂时没有）

综合评价： （暂时没有） 修改稿：

【合金法实现ZnO的P型转化】相关文章：

基于P2P视频点播系统的设计与实现11-23

转化型抢劫罪研究01-04

纤维基ZnO/Ag/ZnO多层膜表面形貌的AFM观察03-07

纤维基ZnO/Ag/ZnO多层膜的制备、结构及性能研究03-07

OMRON公司的C系列P型机对电梯升降控制系统(一)03-07

会计集中核算向管理型和服务型转化论文12-06

基于P2P网络的QoS研究03-07

P2P-SIP网络电话03-28

浅谈会计集中核算向管理型和服务型转化论文12-06